Flange IX Seal Rings
Many clients have drawn on SUNWELL`s specialized knowledge and experience on the use of high pressure and high temperature metal-to-metal static sealing. SUNWELL have developed a sealing system which uses a modified cone ring giving excellent leak tightness properties under the most severe conditions of pressure, temperature, thermal cycling and shock.
IX Seal Rings are designed and used where NORSOK CFC (Compact Flange Connections) are in use.
The rings come in three different kinds of steel and are coated with PTFE in varying colors in order to distinguish between them
(Standard identification NORSOK)
The designed or materials shall be selected, so that main sealing ares can not be subject to corrosion.
Typical Seal Ring Materials:
Typical minimum yield stress and ultimate stress of the seal ring material shall at maximum design temperature be 300MPa and 360MPa, respectively, in order to allow for reasonably elastic spring-back.
Lower strength may be used, but is not recommended.
The user is responsible for selecting a seal ring material which is suitable for the service medium and the design temperature conditions.
Seal ring materials are commonly chosen to be compatible with the flange material,
I.e. Duplex seal ring in duplex flange.
IX Seal Ring Selection: | Flange Material | Service Temp. | Seal Ring Material | Seal Ring PTFE Color | | Carbon Steel | -50oC to +250oC | CS,316L,Low Alloy Steel (AISI4140) | Blue | | Stainless Steel | -50oC to +250oC | 22Cr Duplex | Yellow | | Stainless Steel | -50oC to +250oC | 17/4-PH | Orange | | Stainless Steel | -101oC to +250oC | Nickel Alloys (Inconel 625 etc) | Black | \ n \ nRecubrimiento: \ nIX Los anillos de sello deben estar recubiertos con revestimiento y período de PTFE de 10 μm a 30 μm; El color del recubrimiento debe seguir el requisito de la tabla anterior y el período; \ n \ n Acabado superficial: \ nTodas las superficies de los anillos de mar se mecanizarán con una rugosidad superficial máxima de acuerdo con la tabla siguiente: | Location | Ra max μm | | Sealing Faces | 0,8 | | All other Surfaces | 6,3 | \ n¿Cómo funciona IX Ring Seal Works \ nIX Las fuerzas axiales del anillo de sello se ejercen sobre la conicidad del anillo de sello metálico y se traducen en una fuerza y período de sellado radial; Además, con una mayor precarga, el bisel está cerrado y el contacto cara a cara se logra en la cuña exterior, mientras que la mayor parte de la carga previa del perno se transfiere como fuerzas de compresión entre las caras de brida en el talón y el período; \ n \ nHay dos independientes sellos y período; El primer sello se crea aplicando la tensión de asiento del sello en el talón y el período de la brida; La brida también permanece en contacto a lo largo de su circunferencia exterior en las caras de la brida para todos los niveles y períodos de carga permitidos; El sello principal es el IX Anillo y período del sello; La fuerza del anillo de sellado es proporcionada por la energía elástica almacenada en el anillo y período de sellado tensionado; Cualquier fuga infernal dará presión interna que actuará sobre el anillo de sellado dentro intensificando la acción y el período de sellado; \ nEl diseño tiene como objetivo prevenir la exposición al oxígeno y otros agentes corrosivos y el período; Por lo tanto, esto evita la corrosión de las caras de las bridas, la longitud tensionada de los pernos y el anillo y el período de sellado; \ n \ nIX Instalación de anillo de sello: \ n \ nTamaño y peso: \ nLos anillos IX solo tienen una dimensión por DN & lpar; Diámetro nominal & rpar; que cubre todas las clases de presión | DN | NPS | IX Dimension | Weight (kg) | | 15 | 1/2" | IX15 | 0,02 | | 20 | 3/4" | IX20 | 0,03 | | 25 | 1" | IX25 | 0,03 | | 40 | 1 1/2" | IX40 | 0,05 | | 50 | 2" | IX50 | 0,08 | | 65 | 2 1/2" | IX65 | 0,12 | | 80 | 3" | IX80 | 0,17 | | 100 | 4" | IX100 | 0,28 | | 125 | 5" | IX125 | 0,42 | | 150 | 6" | IX150 | 0,62 | | 200 | 8" | IX200 | 0,99 | | 250 | 10" | IX250 | 1,85 | | 300 | 12" | IX300 | 2,18 | | 350 | 14" | IX350 | 2,60 | | 400 | 16" | IX400 | 3,43 | | 450 | 18" | IX450 | 4,38 | | 500 | 20" | IX500 | 5,27 | | 550 | 22" | IX550 | 6,48 | | 600 | 24" | IX600 | 7,55 | | 650 | 26" | IX650 | 8,74 | | 700 | 28" | IX700 | 10,40 | | 750 | 30" | IX750 | 11,80 | | 800 | 32" | IX800 | 13,30 | | 850 | 34" | IX850 | 14,80 | | 900 | 36" | IX900 | 17,10 | | 950 | 38" | IX950 | 18,90 | | 1000 | 40" | IX1000 | 20,90 | | 1050 | 42" | IX1050 | 23,00 | | 1100 | 44" | IX1100 | 25,10 | | 1150 | 46" | IX1150 | 27,50 | | 1200 | 48" | IX1200 | 29,90 | Características: \ n> Tamaño de 10 mm a 1700 mm actualmente en servicio y semi; \ n> Cuanto mayor es la presión, más atractivo es el diseño de SUNWELL a medida que la presión interna intensifica la acción de sellado y semi; \ n> IX anillo de sello puede estar a altas temperaturas y período; La temperatura máxima de servicio está limitada por el material de sellado seleccionado y el período; Los materiales van desde acero al carbono y aleación hasta inconel, con una gama de recubrimiento para lubricación y semi; \ n> El sistema de sellado es extremadamente hermético bajo las condiciones más severas de presión, temperatura, vacío y es adecuado para aplicaciones nucleares y semi; \ n > Las condiciones de enfriamiento en frío y los ciclos térmicos son la causa de la mayoría de los problemas de fugas donde se utilizan juntas y juntas de tipo compresible convencionales y el período; La flexibilidad adicional del IX Seal Ring garantiza un sellado hermético durante las condiciones térmicas y transitorias; \ n> los diseños de bridas compactos y más ligeros generalmente se pueden lograr utilizando IX Seal Rings & period; Las áreas de sello de fluido y las cargas de juntas son más bajas en comparación con las juntas de tipo compresible convencionales y semi; \ n> El anillo de sello IX es elástico en diseño y en el desmantelamiento vuelve a su forma original listo para reutilización y período; Todos los sellos de un tamaño dado son intercambiables sin ningún preajuste y período; Grupos de Producto : Juntas de juntas de anillo
|